2023-08-10 04:31:48 +00:00
|
|
|
|
---
|
|
|
|
|
|
title: 酸化亜鉛系トランジスタ
|
|
|
|
|
|
tags:
|
|
|
|
|
|
- research
|
|
|
|
|
|
- survey
|
|
|
|
|
|
- semiconductor
|
|
|
|
|
|
---
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
**[[Homemade Thin-Film Transistor Experiments]]**
|
|
|
|
|
|
|
2023-08-14 10:46:10 +00:00
|
|
|
|
前駆体溶液の溶媒は2-プロパノール（っていうかこれイソプロピルアルコールか）
|
2023-08-14 07:45:11 +00:00
|
|
|
|
|
2023-08-10 07:50:08 +00:00
|
|
|
|
[[硝酸亜鉛]]からの生成
|
|
|
|
|
|
|
|
|
|
|
|
[[酢酸亜鉛]]からの方が安心できそう
|
|
|
|
|
|
|
2023-08-10 06:41:47 +00:00
|
|
|
|
[[スプレー熱分解法による酸化亜鉛薄膜の低温大気作製]](2013)
|
|
|
|
|
|
|
|
|
|
|
|
ジエチル亜鉛を溶媒で希釈したものをスプレーで吹き付け、常圧、比較的低温（~200度）での加熱で成膜
|
|
|
|
|
|
|
2023-08-10 04:31:48 +00:00
|
|
|
|
##### 酸化亜鉛薄膜の形成と物性・デバイス応用(2019)
|
|
|
|
|
|
|
|
|
|
|
|
https://www.jstage.jst.go.jp/article/vss/62/7/62_20180376/_pdf/-char/ja
|
|
|
|
|
|
|
|
|
|
|
|
溶液法の説明ある
|
2023-08-10 04:41:48 +00:00
|
|
|
|
|
2023-08-10 04:31:48 +00:00
|
|
|
|
> 酢酸亜鉛とモノエタノ ールアミンを 2-メトキシエタノールに溶かした亜鉛濃度 0.3 mol/L のものを前駆体溶液とし使い酸化亜鉛薄膜を 形成した。前駆体溶液をガラス基板上にスピンコート塗布と中間乾燥を繰り返し，最終焼結を経て成膜が完了する。最終焼結温度を 300℃，400℃，500℃ と変化させて X 線回折測定を行った結果，500℃で c 軸配向が確認さ れ，多結晶膜が形成されていることが分かった。続けてトランジスタを試作すると，c 軸配向が得られた場合に限りトランジスタ動作が確認された。
|
|
|
|
|
|
|
2023-08-14 07:45:11 +00:00
|
|
|
|
> ゾルゲル法では，加熱により中間生成物（水酸化物） を経て，酸化物が形成されるため，中間乾燥工程の温度も膜質に大きな影響を与えると予想される。そこで，最終焼結条件を空気中 500℃，4 時間に固定し，中間乾燥温度のみを 150℃，180℃，240℃，300℃と変化させ， 膜の平坦性と抵抗値を測定し，トランジスタを作製した。その結果，中間乾燥温度が 150℃，180℃ では，膜 の二乗平均粗さが 5 nm を超える粗さを示し，X 線回折 でも c 軸配向した膜は得られず，トランジスタ動作も得られないという結果となった。一方，240℃，300℃ の中間乾燥を経た膜では粗さが 1 nm 程度と平坦でc 軸配 向した膜が得られ，トランジスタ動作が確認された。
|
2023-08-10 04:41:48 +00:00
|
|
|
|
|
2023-08-10 04:31:48 +00:00
|
|
|
|
|
2023-08-10 06:41:47 +00:00
|
|
|
|
[[Pulsed Laser Ablation - A Facile and Low-Temperature Fabrication of Highly Oriented n-Type Zinc Oxide Thin Films]](2022)
|
|
|
|
|
|
|
|
|
|
|
|
大気中でパルスレーザーで成膜
|
|
|
|
|
|
|
|
|
|
|
|
|
2023-08-10 04:31:48 +00:00
|
|
|
|
##### Direct Light Pattern Integration of Low-Temperature Solution-Processed All-Oxide Flexible Electronics
|
|
|
|
|
|
|
2023-09-13 04:10:52 +00:00
|
|
|
|
https://pubs.acs.org/doi/full/10.1021/nn504420r
|
|
|
|
|
|
|
|
|
|
|
|
##### A performance comparison between honey and water as electrolytic dielectrics for ZnO liquid-gated transistors
|
|
|
|
|
|
|
|
|
|
|
|
https://link.springer.com/article/10.1007/s00339-023-06565-6
|
|
|
|
|
|
|
|
|
|
|
|
なぜ蜂蜜を誘電体に使おうと思ったのか、、、
|
|
|
|
|
|
|
|
|
|
|
|
##### Effect of the gate electrodes/water interface on the performance of ZnO-based water gate field-effect transistors
|
|
|
|
|
|
|
|
|
|
|
|
https://www.sciencedirect.com/science/article/abs/pii/S1369800122005741
|
|
|
|
|
|
|
|
|
|
|
|
##### High-mobility low-temperature ZnO transistors with low-voltage operation(2010)
|
|
|
|
|
|
|
|
|
|
|
|
https://doi.org/10.1063/1.3428357
|
|
|
|
|
|
|
|
|
|
|
|
##### Sub-0.5 V Highly Stable Aqueous Salt Gated Metal Oxide Electronics(2015)
|
|
|
|
|
|
|
|
|
|
|
|
https://www.nature.com/articles/srep13088
|
|
|
|
|
|
|
|
|
|
|
|
ゲートをDI Water、NaCl溶液、KCl溶液とかで比べてる
|
|
|
|
|
|
|
2023-09-14 12:15:55 +00:00
|
|
|
|
当たり前だけど直接液体が誘電体に触れちゃダメなのか、うまくZnOのとこにだけ当たるように調整する必要がある
|
|
|
|
|
|
|
|
|
|
|
|
##### Structural and electrical properties of ZnO films prepared by screen printing technique(2005)
|
|
|
|
|
|
|
|
|
|
|
|
https://www.sciencedirect.com/science/article/pii/S0040609000017879
|